Abstract: Electropolishing has various parameters because an electrochemical reaction is applied. Accordingly, experiments to determine factors and levels of electropolishing conditions are in progress for various materials. The purpose of this investigation was to optimize conditions for electropolishing using the taguchi method for UNS S31603. Factors such as electrolyte composition ratio, electrolyte temperature, and electropolishing process time were selected. Electropolishing was optimized using analysis of variance (ANOVA), signal-to-noise ratio (the smaller the better characteristics), and surface analysis. Results of ANOVA revealed that only the electrolyte composition ratio among factors was effective for surface roughness. As a result of statistical analysis of the signal-to-noise ratio, the highest signal-to-noise ratio was calculated under electropolishing conditions with sulfuric acid and phosphoric acid ratio of 4:6, an electrolyte temperature of 75 ℃, and electropolishing process time of 7 minutes. In addition, the surface roughness after electropolishing under the above conditions was 0.121 μm, which was improved by more than 88% compared to mechanical polishing.